Products Detail

UHMW-PE Elbow

没有此类产品
I want to make an inquiry
Description
Features
Specifications
Application

Ultra-high molecular weight polyethylene (UHMWPE) is a kind of engineering thermoplastics with more than 3 million viscosity-average molecular weight. It differs from PE standard grades in its very high degree of polymerization. Ultra-high molecular weight polyethylene

pipe has superior performance over conventional HDPE pipe such as very high wear resistance, impact resistance, intrinsically self-lubricating, anti-adhesion,low temperature resistance and excellent chemical resistance.

 

Can be widely used in metallurgy, mining (mineral mud conveying, backfilling by grouting), power (fly ash conveying), sand dredging pump (lake dredging mud conveying, sand pump pipe of pumping vessel), oil, natural gas, textile, papermaking, food, chemical, mechanical, electrical and other industries.

UHMWPE Elbow dimensions show as below, they that can be equip with PIPE in different conditions:

90 degree elbow60 degree elbow ,30 degree elbow,45 degree elbow, T type elbow

Corresponding parameter set not found, please add it in property template of background
  • 5x lower surface roughness (ISO 8295)
  • Increased temperature capability (particularly in the lower range), capable of -70 to +80 deg C operation
  • Comparable elongation performance
  • Anti-aging agent reduce UV degradation by comparison and otherwise increases design life
  • Colourless, odourless and non-toxic
  • Formed flanges, allowing for clean alignment. Mn16 inserts used at flange end to reduce turbulence down the pipe or bend
  • Much higher corrosion resistivity, comparable to Teflon
  • Higher tensile and yield tolerances
  • Can be provided that make UHMWPE flameproof (allowing for minimal degradation in environments where this is a factor, UHMWPE will still ignite at 300 deg C, but will immediately self-rectify)
  • Lighter and more durable, allowing for heavily reduced installation costs as large excavation and crane equipment will no longer be required
  • Unlike other materials, UHMWPE is self-lubricating (part of why it is used as a ball material for hip joint replacement)
  • All this allows UHMWPE to improve on ANY process currently utilising HDPE and most that include Steel
  • UHMWPE Parts Performance

    Test items

    Unit

    Results

    Test basis

    Tensile yield strength

    Mpa

    34.9

    GB/T 1040-2006

    Tensile breaking strength

    Mpa

    38.8

    GB/T 1040-1992

    IZOD Impact strength

    KJ/m2

    137

    GB/T 1843-1996

    Elongation(sample size :80*10*4mm)

    %

    318

    GB/T 1034-1998

    Heat Deflection Temperature

    96

    GB/T 1663-2000

    Melt Temperature

    236

    GB/T 1634-2001

    Coefficient of friction

    ---

    0.01

    GB/T 0006 -2002

    Ball indentation hardness

    N/mm2

    42.3

    GB/T 3398-1982

    Density

    g/cm3

    0.96

    GB/T 1033-1986

     

          

    1. Dredging project

    2. Mining and metallurgy